OEM 6005A Forging Aluminum Parts For High-Speed Train Carriage /
Transportation Parts/Forging Aluminum/ Forging Parts
Our Advantages
1. 3 technical patents and 2 practical patents related to
high-silicon aluminum alloy melting, crystallization, and forging
2. Multiple professional presses adapted to the deformation speed
of high-silicon aluminum alloys
3. Two intermediate frequency heating furnaces suitable for heating
weak magnetic materials such as high-silicon aluminum alloys
4. Perfect forging process of various pistons and swash plates,
mold tooling technology, materials, and product inspection
standards.
5. The close cooperative relationship between the company and the
university scientific research is our strong technical backing.
6. We are high-tech enterprises
7. Development capability: aluminum alloy, titanium alloy, super
alloy, non-ferrous metal forging development
Product Details
Material | Aluminum Alloy 6005A |
Process | Forging+CNC+Heat Treatment |
Surface Treatment | Transparent / Color Anodized;Hard Anodizing;Powder Coating;
Sandblasting, Laser Carving, Silk Screening;
Nickel-Plated, Chrome, Galvanized, Silver/Gold Plating;
Black Oxide Coating; Polishing; etc... |
Manufacture Ability | Depends on The Complexity Of Different Products And Quantities |
Experience | Aluminum Machining Service for 12 Years |
Packaging | Standard Export Wooden Pallets
Another Request According to Your Need |
MOQ | 1pcs |
Sample | Can Be Customized |
Mold | Can Be Customized |
Lead Time | Mold for 15-20Days Process for 15-20Days |
OEM | Can be Customized |
Chemical Composition of 6005A |
Alloy | Si | Fe | Cu | Mn | Mg | Cr | Zn | Ti | Mn+Cr | Others | Al |
Each | Total |
6005A | 0.5-0.9 | 0.35max | 0.3max | 0.5max | 0.4-0.7 | 0.3max | 0.2max | 0.1max | 0.12-0.50 | 0.05max | 0.15max | Rest |
Technical Specifications
Physical Properties | Metric |
Density | 2.70g/cc |
Mechanical Properties | Metric |
Hardness, Brinell | 95 |
Hardness, Knoop | 120 |
Hardness, Vickers | 107 |
Tensile Strength, Ultimate | 260 MPa |
Tensile Strength, Yield | 240 MPa |
Elongation at Break | 8.0% |
Modulus of Elasticity | 69.0 GPa |
Poissons Ratio | 0.33 |
Fatigue Strength | 100 MPa |
Shear Modulus | 26.0 GPa |
Shear Strength | 205 MPa |
Electrical Properties | Metric |
Electrical Resistivity | 0.00000349 ohm-cm @ 20 °C |
Thermal Properties | Metric |
CTE, linear | 23.4 µm/m-°C |
Specific Heat Capacity | 0.890 J/g-°C |
Thermal Conductivity | 189 W/m-K |
Melting Point | 607.2 - 654 °C |
Solidus | 607.2 °C |
Liquidus | 654 °C |
Processing Properties | Metric |
Annealing Temperature | 414 °C |
Solution Temperature | 546.1 °C |
Aging Temperature | 174 °C |